高耐久PETGフィルム
高耐久PETGフィルム is a thermoplastic polyester film based on polyethylene terephthalate glycol-modified resin. The glycol modification reduces the crystallization tendency of standard PET, producing an amorphous sheet with higher impact resistance and better thermoforming range. The film is supplied in thicknesses from 0.25 mm to 6.0 mm, in widths up to 2.1 m, with clear, colored, and frosted surface options. Impact strength reaches 8 to 12 kJ/m² by Charpy notched testing, and the film resists crazing under repeated flexural loading. High Durability PETG Film is specified for machine guards, signage, protective barriers, and thermoformed components where optical clarity and impact resistance are required together over a long service period.
カスタムフィルムプログラム
高耐久PETGフィルム is supplied under an ODM/OEM arrangement. Thickness, width, surface finish, color, and cut format are set according to the buyer's drawing or performance brief. Clear and tinted grades, matte and anti-glare surfaces, and hard-coated variants are developed and documented against a single approved specification sheet, and the approved sheet governs every production lot.
パフォーマンスプロファイル
衝撃エネルギー吸収
高耐久PETGフィルム absorbs impact energy through ductile deformation rather than brittle fracture. Charpy notched impact values of 8 to 12 kJ/m² are maintained at temperatures from -20°C to 40°C, so the film retains its protective function in outdoor and cold-storage installations where acrylic sheet cracks.
耐曲げ疲労性
フィルムの非晶質構造は、応力による白化を起こすことなく、繰り返しの曲げに耐えます。 ASTM D671 に準拠した曲げ疲労試験では、ひずみ振幅 0.5% で 100,000 サイクル後も亀裂の発生が認められず、ヒンジ付きガード、ディスプレイ固定具、フレキシブル バリア パネルでの使用をサポートしています。
光学的な透明度
クリアグレードの高耐久性 PETG フィルムは、ヘイズ値が 1.0% 未満で可視光の 84% ～ 90% を透過します。表面は室内照明下で 10 年間にわたって黄変せず、UV 安定化グレードは 2,000 時間の促進風化下でも色変化をデルタ E 2.0 以内に抑えます。
耐薬品性および耐洗浄性
このフィルムは、希アルカリ性洗剤、中性洗剤、アルコールベースの消毒剤に耐性があります。芳香族溶剤およびケトンに対する耐性は限られています。これらの化学薬品をベースにした洗浄剤は表面の光沢を除去するため、メンテナンス手順から除外されます。
熱成形範囲
高耐久PETGフィルム forms at 120°C to 160°C with a wide processing window. Deep draws and complex shapes are produced without pre-drying, and the formed part retains impact resistance at the stretched corners. Mold shrinkage is 0.2% to 0.6%, consistent across production runs.
寸法安定性
フィルムは、相対湿度 20% から 80% までの湿度変化にわたってカット寸法を保持します。線熱膨張は 6.5 x 10⁻5/°C でアルミニウムに匹敵し、金属押出材の間にフィルムを取り付けるフレーム設計が簡素化されます。
技術データ
応用分野
購入者の質問
PETG は衝撃用途においてアクリルとどのように比較されますか?
高耐久PETGフィルム provides higher impact resistance than cast acrylic at the same thickness, with Charpy notched values of 8 to 12 kJ/m² against typical acrylic values below 2 kJ/m². Acrylic offers higher surface hardness and better scratch resistance. For barrier and guard applications, PETG is specified; for high-scratch display faces, acrylic or a hard-coated PETG grade is preferred.
熱成形前に乾燥は必要ですか?
高耐久PETGフィルム does not require pre-drying in the normal shop environment. The film absorbs less than 0.2% moisture at 50% relative humidity, and that moisture level does not cause surface defects during forming. If the film has been stored in high humidity for an extended period, a 2-hour dry cycle at 65°C is recommended before forming thick-gauge sheet above 4.0 mm.
どのような切断方法や端面仕上げ方法が適していますか?
フィルムはCNCルーター、レーザー、鋸、またはダイカットによって切断されます。レーザー切断ではエッジは研磨されますが、切断線がわずかに琥珀色になることがあります。鋭い一枚刃ビットを使用したCNCルーティングにより、きれいなエッジが得られます。火炎または溶剤ワイプによるエッジ研磨により、ルーターマークが除去され、目に見える用途向けにエッジが明確になります。
使用中にフィルムをどのようにクリーニングすればよいですか?
柔らかい布と中性洗剤溶液またはアルコールベースの消毒剤を使用して掃除してください。きれいな水ですすぎ、マイクロファイバークロスで乾かしてください。アンモニアベースのガラスクリーナー、アセトン、または研磨パッドは表面を攻撃して透明度を低下させるため使用しないでください。ハードコートグレードの場合は、コーティング供給業者のメンテナンス指示に従ってください。
フィルムを他の素材に貼り付けることはできますか?
高耐久PETGフィルム bonds to rigid substrates with solvent-free PU adhesive, acrylic adhesive tape, or structural acrylic adhesive. Solvent-based adhesives containing ketones or aromatic solvents attack the film surface and cause crazing. Test coupon bonding should be completed before production, particularly where the assembly will be exposed to temperature cycling.
取り扱いおよび保管上の注意
- 高耐久性 PETG フィルム シートは、10°C ～ 30°C の乾燥した場所の剛性パレット上に平らに保管してください。シーツを長時間壁に立てかけないでください。シートは自重で曲がる可能性があります。
- 表面の傷を防ぐため、切断中や取り扱い中は保護マスキングフィルムを貼り付けたままにしてください。フィルム表面への接着剤の転写を防ぐため、納品後 30 日以内にマスキングを剥がしてください。
- フィルムの汚れは柔らかい布と中性洗剤で拭き取ってください。研磨パッド、アンモニアベースのクリーナー、ケトンや芳香族を含む溶剤ベースの製品は表面を損傷します。
- 輸送時や設置時にシート全体をサポートします。薄いゲージのシートの端がサポートされていないと、一点で持ち上げるとたわみ、亀裂が生じる可能性があります。
- 屋外設置の場合は、UV 安定化グレードを指定し、固定システムがパネルの端を拘束することなく 1°C あたり 6.5 x 10⁻⁵ の熱膨張を許容することを確認してください。